微波助磨技术处理某钼矿
Microwave-assisted Grinding of a?Molybdenum Ore
投稿时间:2017-10-14  修订日期:2017-12-08
DOI:
中文关键词:  铜钼矿  微波加热  磨细实验
英文关键词:Copper-molybdenum ore  Microwave heating  Milling experiment
基金项目:
作者单位E-mail
聂琪 昆明冶金高等专科学校矿业学院 jiaoxin12065@126.com 
戈保梁 昆明理工大学国土与资源工程学院 jiaoxin12065@126.com 
张晋禄   
焦鑫   
摘要点击次数: 147
全文下载次数: 183
中文摘要:
      以金堆城低品位铜钼矿为研究对象,取破碎后粒度为-2mm的矿石,分别经常规加热及微波加热预处理,然后水淬骤冷,考察相同磨矿条件不同预处理方式对实验样磨细的影响,通过力学分析经常规加热和微波加热预处理后实验样岩石强度的变化情况,并借助SEM-EDS研究了微波加热对矿石内部产生裂纹的影响。结果表明,对该实验样加热到相同温度时,采用微波加热的预处理方式,更易使实验样磨细。常规加热预处理和微波加热预处理后实验样岩石强度随加热温度的升高都有不同程度的减弱,但采用常规加热预处理方式较微波加热预处理方式岩石强度的减弱程度更大。采用微波加热的预处理方式,当温度达到350℃时,然后进行水淬处理,通过SEM可检测出辉钼矿和黄铜矿与硅酸盐矿物边缘处出现了裂缝。
英文摘要:
      With the low-grade copper-molybdenum ore from Jinduicheng as the research object, conventional heating and microwave heating was employed to previously deal with the crushed ore with a grain size of -2mm, and followed by water quenching. The different pretreatment methods on the sample grinding were investigated under the same grinding conditions. Though mechanical analysis, variation of rock strength after conventional heating pretreatment and microwave heating pretreatment, respectively, was identified. The effect of microwave heating on the cracks in the ore was studied using scanning electron microscope coupled with energy dispersive spectroscope. The results show that with the microwave heating pretreatment the test sample is easier to milling under the same healing temperature condition. With the increasing of heating temperature, after pretreatment, the rock strength is decreased to varying degress. However with microwave heating pretreatment, the weakening extent of rock strength is bigger than that with conventional heating pretreatment. With microwave heating pretreatment, when the temperature reaches 350℃ and followed by water quenching, the intergranular cracks appear on the boundaries between molybdenite, chalcopyrite and silicate minerals by using scanning electron microscope.
查看全文  查看/发表评论  下载PDF阅读器
关闭
版权所有:矿产综合利用
地址:四川省成都市二环路南三段五号   邮政编码:610041
电话:028-85592322  Email:kczl@chinajuornal.net.cn;kczhly@163.com
技术支持:北京勤云科技发展有限公司