利用尾矿制备人造云英石试验研究
Experimental Research on Preparation of Artificial Didymite Using Tailings
  
DOI:
中文关键词:  人造石  尾矿  颗粒大小  力学性能  光泽度  耐酸腐蚀  
英文关键词:Artificial stone  Tailings  Particle size  Mechanical properties  Glossiness  Acid corrosion resistance  
基金项目:天津市自然科学基金项目资助(09JCYBJC04200)
侯艳艳  李酽
中国民航大学理学院;
摘要点击次数: 504
全文下载次数: 15
中文摘要:
      以不饱和聚酯树脂、尾矿为主要原料,在常温常压下浇铸制备了人造云英石板。运用光泽度仪、蔡司偏光显微镜以及傅立叶红外光谱仪等对制得的人造石的结构、光泽度、力学性能,耐腐蚀性进行了测试及观察;研究了不同粒度的尾矿对产品性能的影响。结果表明:随着尾矿颗粒的减小,光泽度呈增大趋势,抗弯强度增大,填料粒度在-325目时,人造石的光泽度为51.46,弯曲强度为70.15MPa;试样经20%H2SO4溶液浸泡后有不同程度的腐蚀,尾矿的颗粒越小,耐腐蚀性越差。
英文摘要:
      Artificial didymite was prepared under normal temperature and pressure using saturated polyester resins and tailings as main raw materials.The structure,glossiness,mechanical properties and corrosion resistance of artificial stone were tested and observed by using infra-red spectrum(IR),gloss meter,zeiss polarizing microscope and so on.The influence of tailings particle size on properties of artificial stone was studied.The results show as the particle size of filler decreases,glossiness tends to increase a...
查看全文  查看/发表评论  下载PDF阅读器
关闭
版权所有:矿产综合利用
地址:四川省成都市二环路南三段五号   邮政编码:610041
电话:028-85592322  Email:kczl@chinajuornal.net.cn;kczhly@163.com
技术支持:北京勤云科技发展有限公司